Akor Stainless, a top-notch stainless steel manufacturer and supplier located in Abuja, Nigeria, has earned a solid reputation for providing high-quality stainless steel products that excel in tough environments. One of their standout offerings is the Stainless Steel U Tube, crafted for optimal heat transfer and fluid flow in industrial applications. Using cutting-edge cold-drawing and bending techniques, these tubes guarantee exceptional dimensional accuracy, a smooth surface finish, and impressive corrosion resistance. Akor Stainless offers Stainless Steel U Tubes in a variety of grades and sizes, all adhering to international standards for use in heat exchangers, condensers, boilers, and other thermal processing equipment across diverse industries.
Stainless Steel U Tubes from Akor Stainless are mainly made up of iron, chromium (16–20%), and nickel (8–12%), with optional molybdenum for added corrosion resistance. Depending on the specific grade—typically 304, 316, or 321—the tubes showcase remarkable resistance to oxidation, high temperatures, and chemical corrosion. On the mechanical side, they boast high tensile strength (around 515–620 MPa), excellent elongation, and toughness, ensuring a long lifespan even under pressure and thermal cycling. The seamless bending and annealing process keeps the wall thickness and grain structure consistent, which helps prevent stress corrosion and enhances mechanical integrity in high-temperature settings.
| Size Range | 10 mm OD to 50.8 mm OD |
| Stainless Steel U Tube Outside Diameter | 6.00 mm to 101.60 mm |
| Wall Thickness | 0.70 mm to 8.00 mm |
| Length | up to 20 m (65.62 ft) Length & Customed Required Length |
| Stainless Steel Heat Exchanger Tube Dimenisons | ASTM, AISI, ASME/ ANSI, JIS, DIN, EN, GB, BS, SUS |
| Standard | ASTM A 213, A 268, A 269, A 789, Equivalent to ASME, EN, JIS Etc. |
| Stainless Steel U tube Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
| 304 | min. | 18.0 | 8.0 | |||||||||
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| 304L | min. | 18.0 | 8.0 | |||||||||
| max. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| 304H | min. | 0.04 | 18.0 | 8.0 | ||||||||
| max. | 0.010 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | |||||
| SS 310 | 0.015 max | 2 max | 0.015 max | 0.020 max | 0.015 max | 24.00 26.00 | 0.10 max | 19.00 21.00 | 54.7 min | |||
| SS 310S | 0.08 max | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 0.75 max | 19.00 21.00 | 53.095 min | |||
| SS 310H | 0.04 0.10 | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 19.00 21.00 | 53.885 min | ||||
| 316 | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316L | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316TI | 0.08 max | 10.00 14.00 | 2.0 max | 0.045 max | 0.030 max | 16.00 18.00 | 0.75 max | 2.00 3.00 | ||||
| 317 | 0.08 max | 2 max | 1 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 57.845 min | ||||
| SS 317L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 min | |||
| SS 321 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 5(C+N) 0.70 max | |||
| SS 321H | 0.04 0.10 | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 4(C+N) 0.70 max | |||
| 347/ 347H | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 20.00 | 9.0013.00 | |||||
| 410 | min. | 11.5 | ||||||||||
| max. | 0.15 | 1.0 | 1.00 | 0.040 | 0.030 | 13.5 | 0.75 | |||||
| 446 | min. | 23.0 | 0.10 | |||||||||
| max. | 0.2 | 1.5 | 0.75 | 0.040 | 0.030 | 30.0 | 0.50 | 0.25 | ||||
| 904L | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| max. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
| Stainless Steel U tube Grade | Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 304/ 304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 304H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 310 / 310S / 310H | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40 % |
| 306/ 316H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 316L | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 317 | 7.9 g/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 321 | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 347 | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35 % |
| 904L | 7.95 g/cm3 | 1350 °C (2460 °F) | Psi 71000 , MPa 490 | Psi 32000 , MPa 220 | 35 % |
Contact us to get a quick quote for your requirement.
Client satisfaction by all means forms the top priority with regard to the quality of our Stainless Steel U Tubes. In pursuit of this objective, all our products are given stringent quality assurance regime, which includes hardness tests, chemical analysis by way of spectro analysis, positive material identification (PMI), flattening tests, micro and macro tests, pitting resistance tests, flaring tests and intergranular corrosion (IGC) tests.
To maintain Stainless Steel U Tubes, regularly clean them with mild soap and water to remove dirt and grime. Avoid harsh chemicals and abrasive cleaners. Inspect for signs of corrosion or damage and address any issues promptly.
Stainless Steel U Tubes are highly resistant to corrosion due to their chromium content. However, under extreme conditions like exposure to harsh chemicals or saltwater, corrosion can still occur over time.
Yes, Stainless Steel U Tubes can be used for natural gas applications. They offer excellent corrosion resistance and durability, making them suitable for handling natural gas in various industrial systems.
Akor Stainless’s Stainless Steel U Tubes find extensive use in industries that demand efficient heat exchange and fluid management. They play a crucial role in heat exchangers, condensers, and boiler systems utilized in power generation, oil refining, chemical processing, and desalination plants. In HVAC and refrigeration systems, they promote compact heat transfer and energy efficiency. Their durability against scaling, corrosion, and high temperatures makes them ideal for marine and pharmaceutical applications.